Zortrax Z-HIPS filament is best for 3D printing large models. Its durability makes it perfect for prototyping machines and functional testing. Compared to standard High Impact Polystyrene, Z-HIPS has been modified to provide your 3D prints with unique semi-mat finish. The material’s surface quality is on par with surfaces of mass produced items. With Z-HIPS you can quickly prototype casings and industrial parts with no post-processing needed. This low-shrinkage material allows you to efficiently run reliable performance tests on models closely resembling final products.
Applications
- functional prototyping
- low volume end-use parts production
- models with large, flat surfaces
- architecture mock-ups
- casings
- mechanical parts prototypes
- consumer products prototypes
Available Colours
- Black
- Grey
- Natural White
For use on: Zortrax M200 | M200 Plus | M300 | M300 Plus | M300 Dual
Functional prototyping
Speed up product design by 3D printing high-end prototypes with Z-HIPS. Reliably test functionality and form of your designs before starting the production.
Smooth semi-mat surface
Z-HIPS prototypes perfectly imitate final products. Semi-mat finish reduces the amount of post-processing needed and masks the layering.
Impact resistance and high durability
Visually stunning, prototypes 3D printed with this polystyrene filament are also suitable for performance and impact tests.
Specifications
| Dedicated for | Container | Weight | Diameter | Extrusion |
|---|---|---|---|---|
| Zortrax M200 | spool | 800 g ±5% | 1.75 mm | Single |
| Zortrax M200 Plus | ||||
| Zortrax M300 | 2000 g ±5% | |||
| Zortrax M300 Plus | ||||
| Zortrax M300 Dual |
| Key Properties | Metric | Imperial | Test Method |
|---|---|---|---|
| Elongation at Break | 7.75% | 7.75% | ISO 527:1998 |
| Shore Hardness (D) | 73.2 | 73.2 | ISO 868:1998 |
| Glass Transition Temperature |
98.68° C | 210° F | ISO 11357-3:2014 |
Zortrax Z-HIPS
Zortrax Z-HIPS 3D printing material is best used for parts and models requiring smooth surface which can be effortlessly post-processed. Its hardness makes it perfect for mechanical prototyping and performance testing. Quality of models 3D printed with Z-HIPS is close to mass-produced objects.